Thermally enhanced flip chip package

ABSTRACT

A thermally conductive planar member is in thermally conductive communication with a flip chip encapsulated within a dielectric material that surrounds portions of the thermally conductive planar member, the flip chip, and a predefined portion of a substrate member. The present invention provides a flip chip package having pick-and-place capability without the thermal resistance disadvantage of capped chip packages.

This application is a division of application No. 08/715,212, filed Sep. 17, 1996, now U.S. Pat. No. 5,726,079 issued Mar. 10, 1998, which is a division of application No. 08/666,155 filed Jun. 19, 1996 now abandoned.

BACKGROUND OF THE INVENTION

1. Technical Field

This invention relates generally to encapsulated flip chips and more particularly to a flip chip package having a thermally conductive member encapsulated with the flip chip.

2. Background Art

Flip chips are small semiconductor dies having terminations all on one side in the form of solder pads or bump contacts. Typically, the surface of the chip has been passivated or otherwise treated. The flip chip derives its name from the practice of flipping, or turning, the chip over after manufacture, prior to attaching the chip to a matching substrate.

Flip chip packages require a cover of some type over the silicon chip to protect it and to provide a large flat surface for pick-and-place operations. However, any cover or encapsulant above the chip increases the thermal resistance path to an ambient environment and, hence, the operational temperature of the chip.

Thermally conductive caps have also been provided for flip chips. Typically, a capped chip has a thin layer of a thermally conductive grease between the chip and the cap. However, it has been found that during thermal cycling, the grease has a tendency to be pumped, or displaced from the interface between the chip and the cap, thus increasing the thermal resistance of the interface.

The present invention is directed to overcoming the problems set forth above. It is desirable to have a flip chip package that provides low thermal resistance, and is economical to manufacture. It is also desirable to have such a flip chip package and method of manufacture that uses conventional transfer mold techniques. It is also desirable to have such a flip chip package that does not require the presence of a thermally conductive grease between the chip and a heat conducting member.

SUMMARY OF THE INVENTION

In accordance with one aspect of the present invention, a flip chip package includes a substrate having a plurality of electrical circuits disposed within the substrate, a flip chip mounted on the substrate in electrical communication with predefined ones of the electrical circuits disposed in the substrate, and a thermally conductive planar member disposed in thermally conductive contact with an upper surface of the flip chip. The flip chip package also includes the substantially rigid dielectric material that surrounds the edge surfaces of the thermally conductive planar member, the edge surfaces of the flip chip, and at least a portion of the substrate.

Other features of the flip chip package embodying the present invention include the thermally conductive planar member having a thickness selected to provide a composite structure with the flip chip that extends a predetermined distance above the substrate.

In accordance with another aspect of the present invention, a method of forming a thermally enhanced flip chip package includes providing a substrate and a flip chip which are connected together such that the electrical contacts on the flip chip are in electrical communication with predetermined ones of the electrical contacts on the substrate. The method also includes providing a thermally conductive planar member which is placed on the upper surface of the flip chip in thermally conductive communication with the upper surface. The assembled planar member, flip chip and substrate are placed in a mold cavity wherein a predefined portion of the substrate cooperates to form a substantially closed cavity. The moldable dielectric material is injected into the closed mold cavity and, after curing, forms a substantially rigid covering about the edges of the thermally conductive planar member, the flip chip, and the predefined portion of the substrate.

Other features of the method of forming a thermally enhanced flip chip package include selecting a thermally conductive planar member having a thickness that is selected so that when the thermally conductive planar member is placed on the flip chip, the combined thickness of the planar member and the distance that the flip chip extends above the surface of the substrate, are substantially equal to the height of the aforementioned mold cavity.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1A is a schematic sectional view of a flip chip package in accordance with a first embodiment of the present invention, showing the flip chip and substrate components of the package in elevation and the dielectric material between the thermally conductive planar member and the flip clip.

FIG. 1B is a schematic sectional view of a flip chip package in accordance with a second embodiment of the present invention, also showing the flip chip and substrate components of the package in elevation and the adhesive material between the thermally conductive planar member and the flip clip; and

FIG. 2 is a flow diagram of the principal steps carried out in forming a flip chip package, in accordance with the method embodying the present invention.

DETAILED DESCRIPTION OF A PRESENTLY PREFERRED EXEMPLARY EMBODIMENT

A flip chip package 10 embodying the present invention, is shown schematically in FIGS. 1A and 1B. The flip chip package 10 includes a flip chip 12 that has a plurality of electrical contacts 14 that are electronically connected, for example by soldered joints, to corresponding contacts associated with one or more electrical circuits disposed in a substrate member 16. The substrate member 16 is typically a laminated circuit board having a number of electrical circuits defined within the member and is adapted for interconnection with other components of an electronic assembly. The flip chip 12 has a planar upper surface 18 that is spaced from the substrate 16 by a predefined distance, and a plurality of edge surfaces 20 that extend around a defined perimeter of the planar surface 18 and are disposed in substantially perpendicular relationship with the planar surface 18.

Importantly, the thermally enhanced flip chip package 10 embodying the present invention includes a thermally conductive planar member 22 that is disposed in thermally conductive communication with the planar upper surface 18 of the flip chip 12. The thermally conductive planar member 22 has a plurality of edge surfaces 24 that extend around the periphery of the planar member 22.

The thermally enhanced flip chip package embodying the present invention also includes a substantially rigid dielectric material 26, such as Toshiba XK6000™ thermoset plastic, that surrounds, in intimate bonded contact, the edge surfaces 24 of the thermally conductive planar member 22, the edge surfaces 20 of the flip chip 12, and at least a portion of the laminated substrate 16. The dielectric material 26 effectively encapsulates the flip chip 12, and a portion of the planar member 22 and the substrate 16, without covering the upper exposed surface of the thermally conductive planar member 22.

In one embodiment of the present invention, it is desirable to form the flip chip package 10 by transfer mold techniques. To reduce the number of molds that may be required to accommodate variously sized chips, the thermally conductive planar members 22 may be formed by stamping from sheets, in a variety of thicknesses, and at very low cost. By using the appropriate thickness of planar member 22, various thicknesses of chips may be accommodated within a single mold. For that purpose, it is desirable that the thermally conductive planar member 22 have a thickness that is selected to provide a composite structure, when mounted on top of the flip chip 12, that extends a fixed predetermined distance above the substrate member 16. Thus, by simply varying the thickness of the planar member 22, the same mold cavity may be used for variously sized chips 12.

In the preferred embodiment, shown in FIG. 1B, the thermally conductive planar member 22 is placed in the mold cavity prior to inserting the flip chip 12 attached to the substrate member 16 into the mold cavity, after which the dielectric material 26 is injected into the cavity. Alternatively, as shown in FIG. 1B, the thermally conductive planar member 22 may be prebonded to the planar upper surface 18 of the flip chip 12 by a thermally conductive adhesive material 28 prior to placing the bonded assembly into the mold cavity and injecting the dielectric material 26 into the cavity.

Preferably, the thermally conductive planar member 22 is formed of copper, which has a thermal coefficient of expansion substantially equal to that of laminated glass-epoxy printed wiring boards.

The method of forming an enhanced flip chip package 10 embodying the present invention includes providing a substrate member 16 having a plurality of electrical contacts disposed on an upper surface of the substrate member, as indicated at block 30 in FIG. 2, and also providing a flip chip 12 having a plurality of electrical contacts 14 disposed on a lower surface, as indicated at block 32. The flip chip 12 is attached to the substrate member 16, as indicated at block 34, typically by a heating cycle in which solder interconnections are formed. If desired, an underfill material such as Dexter's HYSOL™ 4511 epoxy may be used to provide electrical isolation between the connected contacts.

A thermally conductive planar member 22, preferably a copper plate, is provided as indicated at block 36, and then placed on the upper surface 18 of the flip chip 12 so that the planar member 22 is in thermal communication with the upper surface of the flip chip 12, as indicated at block 38, either by intimate contact or by an adhesive bond to the upper surface 18.

The aligned thermally conductive planar member 22, the flip chip 12, and the substrate member 16 are then placed in a mold cavity, as indicated at block 40. A portion of the substrate member 16, i.e., the immediate area surrounding the mounted flip chip 12, cooperates with other predefined surfaces of the mold cavity to form a substantially closed cavity. A moldable dielectric material, such as a highly-filled epoxy, is then injected into the transfer mold, as indicated at block 42, and surrounds the edge surfaces 24 of the planar member 22 and the flip chip 12. As can be seen in FIGS. 1A and 1B, the dielectric material 26 also is forced into intimate contact against a portion of a lower surface of the thermally conductive member 22 and the surrounding area of the surface of the substrate member 16, thus essentially providing effective encapsulation of the flip chip 12 and the thermally conductive planar member 22 with the substrate member 16.

After curing the moldable dielectric material 26, as indicated at block 44, a substantially rigid dielectric covering is thereby formed over the thermally conductive planar member 22, the flip chip 12, and the predefined portion of the substrate member 16, providing an integral, essentially inseparable, package 10. After curing, the formed package 10 is removed from the mold, as indicated at block 46.

Preferably, in carrying out the method of forming a thermally integrated flip chip package 10, a single mold cavity may be advantageously used for a variety of differently sized flip chips 12 by varying the thickness of the planar member 22. If accurately sized, there will be no dielectric material over the top exposed surface of the planar member 22. This is desirable so that the heat conductive path from the flip chip 12 has a minimum number of interfacial resistances in the path of heat flow. Thus, it is desirable to control the thickness of the planar member 22 so that its upper surface is flush with the surface of the mold compound on the finished part. In this arrangement, no adhesive material would be required between the thermally conductive planar member 22 and the flip chip 12, although a thermally conductive adhesive material 28 may be used, if desired, as an assembly aid.

In summary, the flip chip package arrangement and method of forming provides a flip chip package 10 that is reliable in performance and easy to manufacture. These objectives are accomplished by using the transfer mold technique to encapsulate the chip, along with a thermally conductive planar member 22 that is used as an insert during molding. Alternatively, the insert may be attached to the top of the flip chip 12 by use of a small amount of a thermally conductive adhesive material 28.

The planar member 22 may be stamped from sheets, of varying thicknesses, at very low cost. By using the appropriate thickness of insert, any thickness chip can be accommodated within a single mold. The thickness of the planar member 22 should be selected to match the height of the cavity in the mold, when combined with the flip chip 12, to avoid excessive loads on the chip-to-substrate interconnection when the mold is clamped.

The thermal performance of a flip chip package 10 embodying the present invention, preferably without an adhesive layer, will be substantially identical to that of a capped chip, using thermal grease. Furthermore, the flip chip package 10 embodying the present invention has the advantage of avoiding any possibility of pumping which may deplete the grease layer and increase the thermal resistance, as may occur with capped chips. Importantly, the performance of the flip chip package 10 embodying the present invention, is significantly better than that of any package which uses overmold without the thermally conductive planar member 22. In addition, bending of the package 10 is reduced as a result of balancing the expansion of the substrate member 16 and the planar member 22, providing high reliability and improved coplanarity when embodied in a Ball Grid Array (BGA) package.

Although the present invention is described in terms of a preferred exemplary embodiment, those skilled in the art will recognize that changes in the order in which various components, e.g., the substrate member 16, the thermally conductive planar member 22, and the flip chip 12, are provided may be varied without departing from the spirit of invention. Such changes are intended to fall within the scope of the following claims. Other aspects, features, and advantages of the present invention may be obtained from a study of this disclosure and the drawings, along with the appended claims. 

What is claimed is:
 1. A flip chip package, comprising:a substrate member having a plurality of electrical circuits disposed therein; a flip chip mounted on said substrate in electrical communication with some of said plurality of electrical circuits disposed in said substrate, said flip chip having a planar upper surface spaced from said substrate and a plurality of edge surfaces spaced around a defined perimeter of said planar surface in substantially perpendicular relationship with said planar surface; thermally conductive planar member having upper and lower surfaces with a thickness in between said surfaces, said lower surface of said thermally conductive planar member disposed in thermally conductive communication with said planar upper surface of the flip chip and having a plurality of edge surfaces extending around a defined perimeter of the thermally conductive planar member; and a substantially rigid plastic dielectric material surrounding the edge surfaces a substantially rigid plastic dielectric material surrounding the edge surfaces of the thermally conductive planar member, the edge surfaces of said flip chip, and at least a portion of said substrate member, and in between said planar upper surface of the flip chip and said lower surface of said thermally conductive planar member.
 2. A flip chip package, as set forth in claim 1, wherein said flip chip extends above said substrate and under said thermally conductive planar member, said thermally conductive planar member having a thickness which is selectable from a plurality of thicknesses to provide a plurality of flip chip package heights dependent on the thickness of said thermally conductive planar member.
 3. A flip chip package, as set forth in claim 1, wherein said thermally conductive planar member is formed of copper.
 4. A flip chip package, as set forth in claim 1, wherein said substantially rigid plastic dielectric material is the only material in between said planar upper surface of the flip chip and said lower surface of said thermally conductive planar member. 